Preparation of poly(octatriazacane)

ABSTRACT

A polyoctatriazacane molecule is disclosed that has a plurality of octatriazacane groups having the structure 
     
       
         
         
             
             
         
       
     
     and a plurality of divalent bridging groups, each divalent bridging group comprising an aromatic group.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation of co-pending U.S. patent application Ser. No. 14/305,648, filed Jun. 16, 2014. The aforementioned related patent application is herein incorporated by reference in its entirety.

BACKGROUND

The present disclosure relates to methods of making poly(octatriazacane) materials.

New polymer-forming reactions are difficult to design due to strict requirements for efficient, straight-forward, and clean chemistry. Small molecule octatriazacanes have been synthesized previously but have never been explored as a potential polymer-forming reaction. A new and simple polymer forming polycondensation of diamines with paraformaldehyde to poly(hexahydrotriazine)s and poly(hemiaminal)s has been previously described.

These poly(hexahydrotriazine)s exhibited high Young's modulus (˜14.0 GPa for the freestanding films) but are completely amorphous and generally lack free volume within their polymer matrix due to their high crosslink density. Additionally, these polymers suffer from poor yield strength and solubility and electron-deficient monomers do not react to form polymer according to this reaction scheme. Therefore, polymers that are structurally similar to the poly(hexahydrotriazine)s and poly(hemiaminal)s but having improved yield strength and solubility and which might incorporate electron-deficient monomers would be of interest.

A need exists for methods of making new polymers having improved properties and better performance in the areas described above.

SUMMARY

According to one embodiment, a polyoctatriazacane is a molecule having a plurality of octatriazacane groups having the structure

and a plurality of divalent bridging groups, each divalent bridging group comprising an aromatic group. Each divalent bridging group may have the general structure

wherein R¹, R², R³, and R⁴ are each, individually, H, Cl, CN, F, NO₂, SO₃, heterocycles such as imides, benzoxazoles, benzimidazoles, phenylquinoxalines, C_(x)H_(2x+1−y)R⁵ _(y), or C₆H_(5−a)R⁵ _(a), wherein R⁵ is Cl, F, SO₃, C₆H_(5−a)R⁶ _(a), or NH_(3−b)R⁶ _(b), wherein R⁶ is C_(x)H_(2x+1), C_(x)H_(2x), or C₆H₅, where in each instance x is an integer from 1 to 4, y is an integer from 0 to 2x+1, a is an integer from 0 to 5, and b is an integer from 0 to 3; or the general structure

wherein L′ is a divalent linking group selected from the group consisting of *—SO₂—*, *—N(R′)—*, *—N(H)—*, *—CF₂—*, *—C(CF₃)₂—*, *—R″—*, and combinations thereof, wherein R′ and R″ independently comprise at least 1 carbon.

According to another embodiment, a method of forming a polyoctatriazacane may include forming a reaction mixture comprising a i) solvent, ii) a formaldehyde, and iii) a monomer comprising two primary aromatic amine groups; and forming a polyoctatriazacane by adding formic acid to the reaction mixture. In one embodiment, p-phenylenedianiline is reacted with paraformaldehyde and formic acid in DMSO to produce poly-N,N,N-(p-phenylenedianiline)-octatriazacane.

The above-described embodiments and other features and advantages of the present disclosure will be appreciated and understood by those skilled in the art from the following detailed description, drawings, and appended claims

BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWINGS

FIG. 1 is a ¹H-NMR analysis of a polyoctatriazacane according to one embodiment.

DETAILED DESCRIPTION

Methods of making polyoctatriazacanes are described. Polyoctatriazacanes have the general structure

A plurality of trivalent octatriazacane groups are bonded, at the starred bonds, to divalent linking groups having the general structure *—K′—*, where K′ comprises an aromatic group. A polyoctatriazacane according to formula (1) may be made by mixing together a diamine, or a mixture of diamines, having the general structure H₂N—K′—NH₂, where K′ is defined as above, with an aldehyde (i.e. formaldehyde, paraformaldehyde, acetaldehyde, benzaldehyde, etc.), a solvent, and formic acid.

K′ may be a substituted or unsubstituted phenylene group having the general structure of formula (2):

where R¹, R², R³, and R⁴ are each, individually, H, Cl, CN, F, NO₂, SO₃, heterocycles such as imides, benzoxazoles, benzimidazoles, and phenylquinoxalines, C_(x)H_(2x+1−y)R⁵ _(y), or C₆H_(5−a)R⁵ _(a), where R⁵ is Cl, F, SO₃, C₆H_(5−a)R⁶ _(a), or NH_(3−b)R⁶ _(b), where R⁶ is C_(x)H_(2x+1), C_(x)H_(2x), or C₆H₅, where in each instance x is an integer from 1 to 4, y is an integer from 0 to 2x+1, a is an integer from 0 to 5, and b is an integer from 0 to 3. Thus, in addition to an aromatic group, K′ may have fluorine, chlorine, or sulfonate groups. Exemplary diamine reactants of this type include phenylene diamine, a fluoromethyl phenylene diamine such as a phenylene diamine in the para or meta configuration with one to four fluoromethyl groups, each of which may have one to three fluorine atoms, an alkyl fluoromethyl phenylene diamine with a mixture of alkyl and fluoromethyl substituents, or a phenylene triamine with no more than one amino group having substituents, may also be used. For example, tetrakis-(2,3,5,6-trifluoromethyl)-1,4-diamino benzene, bis-(2,5-trifluoromethyl)-1,4-diamino benzene, or 2-fluoromethyl-bis-(3,5-difluoromethyl)-1,4-diamino benzene may be used.

K′ may also be a polynuclear aromatic group, such as a naphthalene group, an acenaphthene group, an acenaphthylene group, a fluorene group, a phenalene group, or an anthracene group, any of which may be substituted at any non-amino carbon atom with substituted or unsubstituted alkyl or aryl groups or halogens, or may be partially saturated (e.g. dialin, tetralin groups). K′ may also be a substituted or unsubstituted indene, indane, or indole group.

K′ may also be a phenyl containing group having the general structure of formula (3)

where R⁷ is a substituted or unsubstituted alkyl, aryl, or polyaromatic group, any of which may be substituted at any non-amino carbon atom with a substituted or unsubstituted alkyl or aryl group, or a halogen. Thus, R⁷ may be SO₂, C_(x)H_(2x−y)R⁵ _(y), or C₆H_(5−a)R⁵ _(a), with x, y, and a defined as above.

K′ may also be a diphenyl group having the formula (4):

wherein L′ is a divalent linking group selected from the group consisting of *—SO₂—*, *—N(R′)—*, *—N(H)—*, *—CF₂—*, *—C(CF₃)₂—*, *—R″—*, and combinations thereof, wherein R′ and R″ independently comprise at least 1 carbon. In an embodiment, R′ and R″ are independently selected from the group consisting of methyl, ethyl, propyl, isopropyl, phenyl, and combinations thereof. For example, L′ may be a linear hydrocarbyl group having from 1 to 4 carbon atoms. Other L′ groups include methylene (*—CH₂—*), isopropylidenyl (*—C(Me)₂—*), and fluorenylidenyl:

A phenylenedianiline such as p-phenylenedianiline may be used as a diamine reactant. A polyoctatriazacane may have a mixture of linking groups of formula (1) and formula (2).

In an embodiment, a polyoctatriazacane is a crosslinked polymer comprising i) a plurality of trivalent octatriazacane groups of formula (1) covalently linked to ii) a plurality of divalent bridging groups K′ according to the descriptions of K′ above. Each starred bond of a given octatriazacane group of formula (1) is covalently linked to a respective one of the bridging groups K′. Additionally, each starred bond of a given bridging group K′ is covalently linked to a respective one of the octatriazacane groups.

Exemplary non-limiting divalent bridging groups include:

and combinations thereof.

The polyoctatriazacanes described herein can further comprise monovalent aromatic groups (referred to herein as diluent groups), which do not participate in chemical crosslinking and therefore can serve to control the crosslink density as well as the physical and mechanical properties of the polyoctatriazacane polymers. Monovalent diluent groups have a structure according to formula (5), formula (6), formula (7), and/or formula (8):

wherein W′ is a monovalent radical selected from the group consisting of *—N(R¹)(R²), *—CF₂—*, *C(CF₃)₂—*, *—OR³, —SR⁴, wherein R¹, R², R³, and R⁴ are independent monovalent radicals comprising at least 1 carbon. The starred bond is linked to a nitrogen of an octatriazacane group.

Non-limiting exemplary diluent groups include:

wherein the starred bond is linked to a nitrogen of an octatriazacane group. Diluent groups can be used singularly or in combination.

A method of preparing a polyoctatriazacane comprising divalent bridging groups comprises forming a mixture comprising i) a monomer comprising two or more primary aromatic amine groups, ii) an optional diluent monomer comprising one aromatic primary amine group, iii) an aldehyde, and iv) a solvent. The mixture is stirred while formic acid is added. Any aldehyde may be used, such as formaldehyde, paraformaldehyde, acetaldehyde, benzaldehyde, or the like. The equivalence ratio of aldehyde to total moles of primary aromatic amine groups (e.g., diamine monomer plus optional monoamine monomer) is preferably about 1:1 to about 1.25:1. Formic acid is generally added in sub-stoichiometric quantities, such as less than 0.8 equivalents, between about 0.1 equivalents and about 0.5 equivalents, for example about 0.5 equivalents.

Non-limiting exemplary monomers comprising two primary aromatic amine groups include 4,4′-methylenedianiline (MDA), 4,4′-(9-fluorenylidene)dianiline (FDA), p-phenylenediamine (PD), 1,5-diaminonaphthalene (15DAN), 1,4-diaminonaphthalene (14DAN), and benzidene, which have the following structures:

Non-limiting exemplary diluent monomers include N,N-dimethyl-p-phenylenediamine (DPD), p-methoxyaniline (MOA), p-(methylthio)aniline (MTA), N,N-dimethyl-1,5-diaminonaphthalene (15DMN), N,N-dimethyl-1,4-diaminonaphthalene (14DMN), and N,N-dimethylbenzidene (DMB), which have the following structures:

The diluent monomer can be used in an amount of 0 mole % to about 75 mole % based on total moles of monomer and diluent monomer.

The solvent can be any suitable solvent. Preferred solvents include dipolar aprotic solvents such as, for example, N-methyl-2-pyrrolidone (NMP), dimethylsulfoxide (DMSO), N,N-dimethylformamide (DMF), N,N-dimethylacetamide (DMA), Propylene carbonate (PC), and propylene glycol methyl ether acetate (PGMEA).

A polyoctatriazacane as described herein may be coated onto a substrate by forming a first mixture comprising i) a monomer comprising two aromatic primary amine groups, ii) an optional diluent monomer comprising one aromatic primary amine group, iii) an aldehyde, and iv) a solvent, coating the mixture on the substrate to form a precursor layer, and then distributing formic acid over the precursor layer to form a polyoctatriazacane coating. The substrate can be any structurally strong substrate, such as a semiconductor wafer (e.g., silicon wafer), most metals, refractory materials, and other polymers. Any suitable coating technique (e.g., spin coating, dip coating, roll coating, spray coating, and the like) may be used. An adhesive bond may be formed in some cases if the first mixture is allowed to, or able to, penetrate into the surface of the substrate before reacting with the formic acid.

In this context, a substrate may be, without limitation, an electronic device, microchip, microelectronic device, printed circuit board, hard disk drive platter, a portion of fluid filter, and portion of a hydrocarbon (e.g., petroleum, natural gas, or petro-chemical) processing facility such as a pipe, pipeline, fluid pumping device, distillation column, a reaction vessel, or storage tank.

The number average molecular weight (Mn) of a polyoctatriazacane can be in a range of 1000 to 100,000, preferably in a range of 1000 to 50,000, and most preferably in a range of 1000 to 20,000.

In one example, 0.050 g of p-phenylenedianiline (0.462 mmol, 1.0 equivalents, purchased from Sigma-Aldrich Co., LLC, of St. Louis, Mo. and stored under nitrogen) and 0.0277 g paraformaldehyde (0.924 mmol, 2.0 equivalents, washed with water, acetone, the diethyl ether, then dried over P₂O₅ prior to use) were combined in a dried vial with stirbar in a nitrogen-filled glovebox with 0.5 mL of dry DMSO (refluxed over CaH₂ for 96 hours prior and then distilled prior to use). Formic acid, 0.004 g, was then added by syringe to the solution (0.231 mmol, 0.5 equivalents). After 10 minutes, an aliquot of the resulting orange solution was taken for ¹H-NMR analysis. FIG. 1 shows the resulting trace, which is consistent with the following reaction scheme:

While the foregoing is directed to embodiments of the present invention, other and further embodiments of the invention may be devised without departing from the basic scope thereof, and the scope thereof is determined by the claims that follow. 

1. A method, comprising: forming a reaction mixture comprising a i) solvent, ii) an aldehyde, and iii) a monomer comprising two primary aromatic amine groups; and forming a polyoctatriazacane by adding formic acid to the reaction mixture.
 2. The method of claim 1, wherein the solvent is selected from the group consisting of N-methylpyrollidone (NMP), propylene carbonate (PC), dimethylacetamide (DMA), dimethylsulfoxide (DMSO), propylene glycol methyl ether acetate (PGMEA), dimethylformamide (DMF), and combinations thereof.
 3. The method of claim 1, wherein the monomer is selected from the group consisting of p-phenylenedianiline, 4,4′-methylenedianiline (MDA), p-phenylenediamine (PD), 4,4′-(9-fluorenylidenyl)dianiline (FDA), and combinations thereof.
 4. The method of claim 1, wherein the polyoctatriazacane comprises: a plurality of octatriazacane groups having the structure

and a plurality of divalent bridging groups, each divalent bridging group comprising an aromatic group, wherein each divalent bridging group is covalently bonded to an octatriazacane group at one of the starred bonds.
 5. The method of claim 4, wherein each divalent bridging group has the general structure

wherein R¹, R², R³, and R⁴ are each, individually, H, Cl, CN, F, NO₂, SO₃, imides, benzoxazoles, benzimidazoles, phenylquinoxalines, C_(x)H_(2x+1−y)R⁵ _(y), or C₆H_(5−a)R⁵ _(a), wherein R⁵ is Cl, F, SO₃, C₆H_(5−a)R⁶ _(a), or NH_(3−b)R⁶ _(b), wherein R⁶ is C_(x)H_(2x+1), C_(x)H_(2x), or C₆H₅, where in each instance x is an integer from 1 to 4, y is an integer from 0 to 2x+1, a is an integer from 0 to 5, and b is an integer from 0 to 3; or the general structure

wherein L′ is a divalent linking group selected from the group consisting of *—SO₂—*, *—N(R′)—*, *—N(H)—*, *—CF₂—*, *—C(CF₃)₂)—*, *—R″—*, and combinations thereof, wherein R′ and R″ independently comprise at least 1 carbon.
 6. The method of claim 5, wherein the divalent linking group comprises fluorine.
 7. The method of claim 5, wherein L′ is a hydrocarbyl group having from 1 to 4 carbon atoms.
 8. The method of claim 5, wherein the aldehyde is formaldehyde or paraformaldehyde.
 9. The method of claim 1, wherein the reaction mixture is coated onto a substrate before adding the formic acid.
 10. The method of claim 4, wherein the polyoctatriazacane further comprises a plurality of diluent groups having a structure selected from the group consisting of

wherein W′ is a monovalent radical selected from the group consisting of —N(R1)(R2), —OR3, and —SR4, wherein R1, R2, R3, and R4 are independent monovalent radicals comprising at least 1 carbon, and wherein the starred bond is linked to a nitrogen of an octatriazacane group.
 11. The method of claim 10, wherein the diluent group is: 